铋基碘氧化物/活性炭制备及光催化活性研究
张翠红,李 江,陈志敏,郭丽君
太原工业学院 化学与化工系,山西 太原 03000
Research on preparation of bismuth iodide/activated carbon and photo-catalytic activity
Zhang Cuihong, Li Jiang, Chen Zhimin, Guo Lijun
Department of Chemistry and Chemical Engineering, Taiyuan Institute of Technology, Taiyuan 030008, China
摘要 采用超声波法,以活性炭为载体制备了铋基碘氧化物/活性炭粉体催化剂,用偶氮类染料甲基橙模拟印染废水,氙灯为光源,考察了催化剂的光催化活性。实验结果表明:当甲基橙溶液初始pH=4、溶液初始浓度为25 mg/L、催化剂投加量为0.1 g/100 mL、加入1 mL 30%H2O2时,铋基碘氧化物/活性炭催化剂对甲基橙降解效果最优,降解率可达到98.20%;同时研究表明H2O2对铋基碘氧化物/活性炭催化剂光降解甲基橙具有促进作用。
关键词 :
光催化 ,
铋基碘氧化物 ,
活性炭 ,
甲基橙
Abstract :Bismuth-based iodine oxide/activated carbon powder catalyst was prepared by means of ultrasonic method through using activated carbon as carrier. At the same time, its photo-catalytic activity was evaluated using methyl orange as the degradation object, xenon lamp as light source. The results showed that the optimum degradation rate was 98.20% when methyl orange initial concentration was 25 mg/L, initial pH=4, catalyst dosage was 0.1 g/100 mL and 1 mL 30% hydrogen peroxide was added. In addtion, hydrogen peroxide could promote the degradation of methyl orange by bismuth-based iodine oxide /activated carbon catalyst.
Key words :
photo-catalytic
bismuth-based iodine oxide
activated carbon
methyl orange
作者简介 : 张翠红( 1976— ),女,山西阳泉人,副教授。
[ 1 ] 罗善霞. Bi2WO6和掺杂与负载型TiO2光催化剂的制备与表征及其活性评价[ D ]. 天津:天津大学,2010:4.
[ 2 ] 牛新书,许亚杰. 二氧化钛纳米材料的合成及其在环保领域的应用研究进展[ J ]. 化工环保,2002,22( 4 ):205 - 207.
[ 3 ] 郭凯旋. 超声/微波辅助溶胶凝胶法制备TiO2及其性能研究[ D ]. 太原:中北大学,2015:1.
[ 4 ] 张翠红,李 江,陈志敏,等. TiO2/SiO2的制备及光催化氧化降解甲基橙[ J ]. 中北大学学报(自然科学版),2015,36( 6 ):682 - 688.
[ 5 ] 周建伟. 铋系半导体光催化剂及其应用研究进展[ J ]. 化学工程师,2007,21( 12 ):34 - 37.
[ 6 ] 李 燕,杨旭光,孙道胜,等. 铋基碘氧化物/煤矸石复合粉体的制备及光催化性能[ J ]. 人工晶体学报,2016( 2 ):430 - 434.
[ 7 ] 魏平玉,杨青林,郭 林. 卤氧化铋化合物光催化剂[ J ]. 化学进展,2009( 9 ):1 734 - 1 741.
[ 8 ] Zhang K L, Liu C M, Huang F Q, et al. Study of the electronic structure and photocatalytic activity of the BiOCl photocatalyst[ J ]. Applied Catalysis B Environmental, 2006, 68(3 - 4): 125 - 129.
[ 9 ] Wang C, Shao C, Liu Y, et al. Photocatalytic properties BiOCl and Bi2O3, nanofibers prepared by electrospinning[ J ]. Scripta Materialia, 2008, 59( 3 ): 332 - 335.
[ 10 ] Lin X P, Huang F Q, Wang W D, et al. A novel photocatalyst BiSbO4, for degradation of methylene blue[ J ]. Applied Catalysis A General, 2006, 307( 2 ): 257 - 262.
[ 11 ] 谢立进. 铋系复合氧化物纳米晶光催化剂的制备及表征[ D ]. 青岛:中国海洋大学,2006.
[ 12 ] 许效红,姚伟峰,张 寅,等. 钛酸铋系化合物的光催化性能研究[ J ]. 化学学报,2005,63( 1 ):5 - 10.
[ 13 ] 戈 磊,崔立山. 新型可见光活性氧化钯/钒酸铋复合光催化剂的制备及其光催化性能[ J ]. 硅酸盐学报,2008,36( 3 ):320 - 324.
[ 14 ] 王 旭. 铋基碘氧化物基光催化材料的制备及光降解性能研究[ D ]. 哈尔滨:哈尔滨工业大学,2012.
[ 15 ] 林 慧,高荣杰,冯欣欣,等. 沸石负载型Cu2O 光催化剂降解甲基橙[ J ]. 环境工程学报,2015,9( 4 ): 1 783 - 1 788.
[1]
张 高1,周艳丽2. 臭氧协同光催化降解氨氮废水研究 [J]. 煤炭与化工, 2020, 43(7): 152-156.
[2]
李 江,毕佳欣,韩晔娇. EDTA络合亚铁离子活化过硫酸盐降解甲基橙 [J]. 煤炭与化工, 2020, 43(12): 147-150.
[3]
白凯鹏,周利君,曹孟雪,张思锐,徐 杰. 新型钒氧簇-氮杂配体配合物的合成及光催化降解亚甲基蓝染料废水 [J]. 煤炭与化工, 2019, 42(8): 126-127,130.
[4]
尚 曼1,张文亮1,黄 军2,张筱青1,辛 畅3,于宏伟3. 甲基橙皮苷的研究进展 [J]. 煤炭与化工, 2019, 42(7): 121-123,149.
[5]
耿悠然,国 洁. 新型光催化材料的分类 [J]. 煤炭与化工, 2019, 42(2): 126-128.
[6]
胡 莹. 活性炭再生技术研究与发展 [J]. 煤炭与化工, 2018, 41(4): 136-139.
[7]
傅修军,陈志勇,苏景裕,王 楠. 脱H2S用活性炭的制备及样品性能研究 [J]. 煤炭与化工, 2018, 41(10): 142-145.
[8]
申宏丹,孙开进,项东升,颜淑芹. 活性炭吸附硝基苯乙酮同分异构体的研究 [J]. 煤炭与化工, 2017, 40(7): 19-21,152.
[9]
吴 超,傅修军,郑 环,李 强,牛翰彬. 煤基载银活性炭的制备及性能研究 [J]. 煤炭与化工, 2017, 40(11): 49-52.
[10]
周鹏飞,王子杰,张 硕,孙 洲. 凹凸棒土-稻壳活性炭复合滤料与陶粒滤料对水中亚甲基蓝的吸附性能研究 [J]. 煤炭与化工, 2017, 40(10): 11-15.
[11]
宋桂贤,吴雄岗. 可见光响应光催化剂还原CO2 研究进展 [J]. 煤炭与化工, 2016, 39(6): 30-33,43.
[12]
罗 晓,郝彤遥,赵 彦,岳 琳. 石墨烯基S掺杂TiO2 光催化降解罗红霉素的研究 [J]. 煤炭与化工, 2016, 39(10): 1-7.
[13]
史建春,张 鹏,李 雪,梁伟朝,张微微,杨 昆. 离子液体、镧双改性菌渣活性炭吸附—催化氧化二氧化硫研究 [J]. 煤炭与化工, 2015, 38(12): 25-27,76.
[14]
李东霞,李桂明. 乙炔法合成醋酸乙烯催化剂研究进展 [J]. 煤炭与化工, 2015, 38(10): 39-44.
[15]
谢 添,韩相奎, 王晓玲,董利鹏, 张 芳,胡佳欣. 颗粒活性炭吸附法深度处理煤化工废水研究 [J]. 煤炭与化工, 2015, 38(1): 156-157,160.