添加剂对沉淀碳酸钙粒子形成的影响

摘要
图/表
参考文献
相关文章 (3)

全文: PDF (0 KB) HTML (0 KB)
输出: BibTeX | EndNote (RIS)

摘要

分别叙述了无机添加剂、有机添加剂、复合添加剂等对沉淀碳酸钙微细粒子形成的影响。指出由于各种反应条件、添加剂、碳化模式的影响和相互作用，采用碳酸化法的模拟生物矿化可制备出不同晶型和不同形貌的微细碳酸钙粒子；沉淀碳酸钙经历了氢氧化钙与CO2反应生成不定型碳酸钙，不定型碳酸钙向方解石型、文石型、球霰型碳酸钙转变的过程；球霰型碳酸钙的稳定性等是今后研究工作中值得关注的问题。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李占远

关键词 ：沉淀碳酸钙, 添加剂, 晶型

Abstract：

The influences of inorganic additive, organic additive, compound additive on the formation of the precipitated calcium carbonate superfine particle were introduced.It was pointed out that due to the influences and interaction of various reaction conditions，additives and carbonation model, the fine calcium carbonate particles of different crystal and different morphologies were prepared through the biomineralization of carbonation method.Precipitated calcium carbonate has gone through the process of calcium hydroxide reacting with carbon dioxide to generate amorphous calcium carbonate,amorphous calcium carbonate turning into calcite or aragonite or graupel type calcium carbonate.The stability of the vaterite calcium carbonate is worthy of attention in future research work.

Key words： precipitated calcium carbonate additive crystal form

作者简介: 李占远（1959— ），男，河北辛集人，高级工程师。E-mail：83290099sskzlym@163.com

引用本文:

李占远. 添加剂对沉淀碳酸钙粒子形成的影响[J]. 煤炭与化工, 2013, 36(4): 51-54. LI Zhan-yuan. Influences of Additives on Precipitated Calcium carbonate Particles. CCI, 2013, 36(4): 51-54.

链接本文:

http://www.mtyhg.com.cn/CN/ 或 http://www.mtyhg.com.cn/CN/Y2013/V36/I4/51

[ 1 ]     CY Tai, PC Chen. Nucleation, agglomeration and crystal morphologyof calcium carbonate[ J ]. AIChE J, 1995,41（ 1 ）：68 - 77.

[ 2 ]     H Yagi, A Iwazawa, R Sonobe, et al. Crystallizationof calcium carbonate accompanying chemical absorption[ J ]. J Am Chem. Soc, 1984,79 （26 ）：2 031 - 2 034.

[ 3 ]     O Sohnel, JW Mullin. Precipitation of calcium carbonate[ J ]. J Cryst Growth, 1982,60 （ 25 ）：239 - 250.

[ 4 ]     K De Groot, E M Duyvis.Crystal form of precipitate calcium carbonateas influenced by absorbed magnesium ions[ J ]. Nature , 1966,212（ 78 ）：183 - 186.

[ 5 ]     李    纠，陈华雄. 以氯化镁为晶型控制剂制备碳酸钙晶须[ J ].硅酸盐学报，2005，33（ 9 ）：1 153-1 156.

[ 6 ]     陈华雄，宋永才. 文石型碳酸钙晶须的制备研究[ J ]. 材料科学与工程学报，2004，22（ 2 ）：197-200.

[ 7 ]     Woon Kyoung Park, Sang-Jin Ko, Seung Woo Lee, et al. Effects of magnesium chloride and organic additives on the synthesis of aragonite precipitated calcium carbonate[ J ]. J Crystal Growth, 2008，310（ 1 ）：2 593 - 2 601.

[ 8 ]     S Ghizellaoui, M Euvrard. Assessing the effect of zinc on the crystallization of calcium carbonate[ J ]. Desalination, 2008,220（ 1 ）：394 - 402.

[ 9 ]     胡琳娜，何豫基，宋宝俊. 多种晶型微细碳酸钙研制[ J ]. 非金属矿，2001，24（ 3 ）：10 - 12.

[ 10 ]   卫志贤，郑    岚，刘荣杰. 超细碳酸钙的制备[ J ]. 化工进展，1998，5（ 1 ）：50 - 53.

[ 11 ]    L Xiang, Y Xiang, Z G Wang, et al. Influence of chemical additives on the formation of super-fine calcium carbonate[ J ]. Powder Technology, 2002, 126（ 1 ）：129 - 133.

[ 12 ]   HE En-guang, SHANG Wen-yu, CHEN Shou-tian. Effects of Phosphate Ion on the Growth of Aragonite Whisker in Heterogeneous Precipitation from Suspension of Ca(OH)2[ J ]. Raremetal Materials and Engineering，2000，29（ 6 ）：398 - 402.

[ 13 ]     马    洁，李春忠. 焦磷酸钠对液相碳化法制备纳米碳酸钙形貌的影响[ J ]. 无机化学学报，2005，21（ 10 ）：1 465 - 1 470.

[ 14 ]    王仲军. 针状纳米碳酸钙制备研究[ J ]. 非金属矿，2006，29（ 3 ）：29 - 30.

[ 15 ]    马    洁，李春忠. 糖类添加剂对纳米碳酸钙形貌的影响[ J ]. 华东理工大学学报（自然科学版），2005，31（ 6 ）：817 - 820.

[ 16 ]   Jasminka Kontrec, Damir Kralj. Influence of some polysaccharides on the production of calcium carbonate filler particles[ J ]. J CrystalGrowth ,Accepted.

[ 17 ]    蒋惠亮，殷福珊. 表面活性剂对纳米碳酸钙结晶过程的影响[ J ]. 日用化学工业，2005，35（ 2 ）：69 - 71.

[ 18 ]    陈先勇，唐    琴. 单分散球形纳米碳酸钙制备研究[ J ]. 非金属矿，2005，28（ 2 ）：1 - 3.

[ 19 ]    刘海弟，赵融芳，陈运法.利用腐植酸调控碳酸钙微晶形貌及比表面积[ J ]. 过程工程学报，2006，6（ 2 ）：219 - 222.

[ 20 ]    Ian D Cunningham, Jean-Philippe Courtois, et al. Evidence for a fragmentation mechanism during the formation of calcium carbonate organo-nano-particles[ J ]. Colloids Surf Physicochem Eng Aspects， 2007，301（ 1 ）：184 - 188.

[ 21 ]    董鹏飞，胡琳娜，陈树东, 等. 竞争原位制备活性碳酸钙[ J ].河北工业大学学报，2008，37（ 6 ）：37-40.

[ 22 ]   ZHAO Dong-an, XIANG Na-chen, et al. Structure transition from aragonite to vaterite and calcite by the assistance of SDBS[ J ]. Colloid Interface Sci, 2008, 325（ 1 ）：331 - 336.