煤基吸附剂制备及其性能优化研究
王 萌，牛雪杰，姚 剑，李宁亚
河北煤炭科学研究院 洗煤技术研究所，河北 邢台 054000
Coal based adsorbent preparation and performance optimization research
Wang Meng, Niu Xuejie, Yao Jian, Li Ningya
Hebei Coal Science Research Institute，Coal washing technology institute，Xingtai 054000, China
摘要 以神府煤和污水污泥为原料采用微波炭化法制备吸附剂，分别考察了污泥和煤质量比、微波功率、微波炭化时间、碱炭比、活化温度和活化时间对活性炭吸附性能的影响。借助孔结构分析和模拟废水处理试验，对产品的性能进行了表征。结果表明：微波功率为800 W，炭化时间为12 min，碱炭比为3∶1，活化温度为550℃，活化时间为2 h时制取的活性炭的吸附性能较好，碘吸附值为786.36 mg/g，BET比表面积251.78 m2/g，对模拟染料废水脱色率为67%。
关键词 ：
煤 ,
城市污泥 ,
微波 ,
吸附剂
Abstract ：Shenfu ultrafine coal powder and urban sewage sludgeas as the adsorbent preparation materials by microwave carbonization method. Investigates the sludge and coal mass ratio, microwave power, microwave carbonization time, alkali carbon ratio, activation temperature and activation time on the adsorption properties of activated carbon. Performance of the absorbent was characterized based on pore structure analysis and simulated wastewater treatment experiment. It was shown that appropriate microwave power for the adsorbent preparation is 800 W， carbonization time 12 min， alkali to carbon ratio 3:1,activation temperature 550℃,activation time 2 h， iodine value of the corresponding adsorbent is 786.36 mg/g，BET surface area is 251.78 m2/g，dye wastewater removal rate is 67%.
Key words ：
coal
urban sewage sludge
microwave
absorbent
作者简介 : 王 萌（1986—），男，河北邢台人，助理工程师，硕士学位。
[ 1 ] 池勇志，迟季平，马 颜，等. 城镇污水污泥性质与处理处置概况[ J ]. 环境科学与技术，2010，33（12 ）：169-172.
[1]
蔡 超. 益新煤矿石头河子组沉积环境及其聚煤特征
[2]
贾永杰. 综放回采工作面矿压显现规律研究
[3]
苗晓伟，刘前进. 富水顶板特厚煤层两柱和四柱综放支架适应性分析
[4]
宋光升，秦立涛，李聚伏. 郭二庄井田煤岩对比方法研究
[5]
周 科，王炳强. 隔水层等效厚度的评价确定
[6]
武振峰. 云驾岭矿煤泥水处理系统技术改造
[7]
郑晓东. 隔膜压滤机在斜沟选煤厂的应用实践
[8]
安柏忠. 综放面大断面切眼支护技术研究
[9]
马 杰. KJ972型煤与瓦斯突出预警系统在大社矿的应用
[10]
赵智胜. 电牵引采煤机常见电气故障判断及处理
[11]
张计林. 煤质分析常见问题及对策
[12]
张炳义. 薄煤层螺旋钻开采钻采宽度和煤柱宽度的研究
[13]
张欣钊，王 轶，刘迎宾，武亚东. 煤矿加固用聚氨酯材料的力学性能影响因素分析
[14]
郑晓东. 粗煤泥分选技术在斜沟选煤厂的应用
[15]
贾文志. 三维立体图生成法在煤堆测量工作中的应用分析