| Study on properties of glass fiber reinforced modified polyformaldehyde |
| Wang Dong1,2， Yin Lijing1,2， Xie Yunfeng1,2 |
| 1. Tangshan Zhonghao Chemical Corporation Ltd., Tangshan 063611, China; 2. Hebei Provincial Technology Research Center of Coal-based Fine Chemical, Tangshan 063611, China |
|
|
|
|
Abstract Two kinds of polyformaldehyde (POM) with different fluidity were reinforced by short glass fiber (GF), the changes of mechanical properties of the two modified products were analyzed. The research shows that when K90 coformaldehyde is used as the base material, although the reinforcement effect is more obvious, the melt index (MI) decreases more, and the processing fluidity becomes worse; K270 coformaldehyde with good fluidity is selected as the base materia, when the amount of glass fiber added is between 20%~25%, the product has good fluidity and is suitable for the development of reinforced modified products. Glass fiber has a good reinforcing effect on POM, its tensile strength was increased from 62 MPa to 120 MPa， the tensile modulus was increased from 2 599 MPa to 8 950 MPa, nearly three times higher, and the bending strength was increased from 79 MPa to 176 MPa. Moreover, the impact performance of the product is little affected by the addition of glass fiber, which can be maintained at 7.0 KJ/m2, and the effect of reinforcement and modification is very ideal.
|
|
|
|
|
|
| [ 1 ] KUTZ M. Applied plastics engineering handbook[ M ]. 2nd ed Amsterdam: Elsevier Inc, 2017: 443 - 487.
[ 2 ] 李刚键，乃国星，张利军，等. 玻纤增强共聚甲醛性能研究[ J ]. 合成材料老化与应用，2019，48（ 6 ）：21 - 23,71.
[ 3 ] 马小丰，金 旺，杨大志，等. 碳纤维增强聚甲醛复合材料的制备及性能研究[ J ]. 工程塑料应用，2014，42（ 1 ）：23 - 26.
[ 4 ] 刘 娜，李宝龙，李树材. POM/TPU 共混合金的增韧与断裂行为研究[ J ]. 塑料工业，2014，42（ 9 ）：27 - 31.
[ 5 ] 孟永智，方 伟，孙亚楠，等. 聚氨酯弹性体增韧聚甲醛改性研究[ J ]. 合成材料老化与应用，2015，44（ 5 ）：45 - 48.
[ 6 ] 庞绍龙，林桂芳. 工程塑料聚甲醛的生产及其应用研究[ J ]. 化学工程与装备，2010（ 3 ）：120 - 122.
[ 7 ] 何 园，刘保英，房晓敏，等. 聚甲醛增强改性研究进展 [ J ]. 中国塑料，2015，29（ 9 ）：6 - 11.
[ 8 ] TAO Z Z, WANG Y T, LI J H, et al. Fabrication of long glass fiber reinforced polyacetal composites: mechanical performance, microstructures, and isothermal crystallization kinetics[ J ]. Polymer Composites, 2015, 36( 10 ): 1 826 - 1 839.
[ 9 ] ZHANG Y Y, ZHU S W, LIU Y, et al. The mechanical and tribol-
ogical properties of nitric acid-treated carbon fiber-reinforced polyoxymethylene composites [ J ]. Journal of Applied Polymer Science, 2015, 132( 15 ): 41 812．
[ 10 ] BLEDZKI A K, MAMUN A A, FELDMANN M．Polyoxymethyle-
ne composites with natural and cellulose fibres: toughness and heat deflection temperature [ J ]. Composites Science and Technology, 2012, 72( 15 ): 1 870 - 1 874．
[ 11 ] 王彦辉，田庆丰，刘保英，等.硅灰石纤维增强聚甲醛复合材料的制备与性能研究[ J ]. 化学研究，2016，27（ 5 ）：609 - 613．
[ 12 ] LIU B Y，LIU Z，WANG X J，et al．Interfacial shear strength of Carbon fiber reinforced polyphenylene sulfide measured by the microbond test [ J ]. Polymer Testing，2013, 32( 4 ): 724 - 730． |
|
|
|