| Preparation of oxidized polyethylene wax lotion and its application in waterborne industrial paint |
| Xu Heliang1, Duan Xinfeng2 |
| 1. Guangdong Shanmeng New Materials Corporation Ltd., Dongguan 523808, China; 2. Hengshui Dongming Chemical Corporation Ltd., Hengshui 053902, China |
|
|
|
|
Abstract In order to prepare an oxidized polyethylene wax lotion with high content and appearance close to transparency, self-made emulsifier was creatively used to prepare oxidized polyethylene wax lotion by using oxidized polyethylene wax solid wax as the main component and high shear at room temperature. The effects of emulsifier amount, emulsification time and emulsification temperature on the performance of lotion were discussed. The results showed that 30% of emulsifier amount (compared with OPE solid wax) was used, and the emulsification temperature was 130 ~ 135 ℃, The shear speed is 100 ~ 1 500 r/min, and the emulsification time is 1 h. The oxidized polyethylene wax lotion with better performance can be obtained. The performance of the lotion prepared by this formula process is close to that of the lotion prepared under high temperature and high pressure. The performance of the optimized product was compared and tested, and its application in the field of water-based industrial paint was briefly discussed.
|
|
|
|
|
|
| [ 1 ] 段新峰，刘佳宁. 水性OPE蜡乳液的制备及应用[ J ]. 煤炭与
化工，2020，43（ 8 ）：134 - 137.
[ 2 ] 程振锋，张俊文. 无助剂的造纸用氧化聚乙烯蜡乳液的常压制备[ J ]. 胶体与聚合物，2019，37（4）：172 - 175.
[ 3 ] 文水平. 氧化聚乙烯蜡微乳液的制备[ J ]. 印染助剂，2007（ 6 ）：24 - 27.
[ 4 ] 王宇玲. 氧化聚乙烯可作低定量纸的助留剂[ J ]. 国际造纸，1986（ 5 ）：59 - 61.
[ 5 ] 张小丽. 水性氧化聚乙烯蜡在纸质文物保护中的应用[ J ]. 纸和造纸，2011，30（ 2 ）：85 - 86.
[ 6 ] 陈守龙. 氧化聚乙烯用于单面涂布白纸板的背面施胶[ J ]. 北方造纸，1996（ 1 ）：64 - 67.
[ 7 ] 徐秀雯，李 明. 氧化聚乙烯类柔软剂整理织物的折皱回复角的测定和整理效果的探讨[ J ]. 苏州丝绸工学院学报，1994（ 1 ）：28 - 34.
[ 8 ] 强西怀，董艳勇，张 辉. 氧化聚乙烯蜡乳液的制备及在皮革涂饰中的应用[ J ]. 皮革科学与工程，2010，20（ 2 ）：50 - 54.
[ 9 ] 马玉英. 塑料加工用脱模剂的选择和应用[ J ]. 郑州工业高等专科学校学报，2004（ 2 ）：21 - 22，38.
[ 10 ] 张胜文，何立凡，李效玉. 蜡助剂在水性木器涂料中的应用[ J ]. 涂料工业，2007（ 10 ）：62 - 66. |
|
|
|